Product Introduction
流动润滑剂
|
产品 |
主要组分 |
优点 |
应用行业 |
|
FA520A |
超支化聚酯化合物 |
高效提高流动性能 |
PA6,PA66,高温尼龙，长铸足龙 |
|
F1530A |
有机硅氧化物聚合物 |
高效得脱模性能 |
PA,PBTPET,PC+纤，ABS+纤 |
|
FE550A |
乙烯丙烯酸共聚物 |
提高光泽，增加脱模性，很好得国滑 |
PA,PBT,PETPC+F,ABS+纤 |
|
GF |
FE 550A |
|
Tensile Strength in yeild(MPa) |
Tensile Strain (%) |
Flexual modulus (MPa) |
Flexual strength (MPa) |
Notched zod (J/m) |
HDT(C) |
| montan- Wax | ||||||||
|
40 |
- |
- |
180.2 |
2.46 |
10944.07 |
264.24 |
113.239 |
210.4 |
|
40 |
0.8 |
- |
179.04 |
2.4 |
11189.17 |
253.91 |
113.634 |
211.8 |
|
40 |
- |
0.8 |
182.43 |
2.13 |
11575.62 |
245.24 |
109.099 |
211.9 |
FE550A 在PET+ 玻纤中应用
|
GF |
FE550A |
|
Tensile Strength in yeild(MPa) |
Tensile Strain (%) |
Flexual modulus (MPa) |
Flexual strength (MPa) |
Notched zod (J/m) |
HDT(℃) |
| montan- WaX | ||||||||
|
40 |
- | - |
143.98 |
2.41 |
11960.63 |
213.04 |
76.873 |
77.5 |
|
40 |
0.8 |
- |
139.2 |
3.06 |
11611.57 |
216.74 |
98.266 |
77.2 |
|
40 |
- |
0.8 |
139.71 |
1.98 |
12529.85 |
222.41 |
76.341 |
77.3 |
其作用工作原理见图
本品主要适合于聚酰胺系列(PA6 、PA66、PA6T、PA9T、PA1OT等高温尼龙、长链尼龙)。
▶▶ FA520A特 性
分子结构：超支化结构；主体分子通式：CnlHn2On3; 分子量：250-600;目数：40-200目， 支化度0.61-0.72,分解温度：386.4 ℃,密度：1.3000g/cm。