Product Introduction
Flow Lubricant Series
|
Product |
Main Component |
Performance Advantage |
Application Field |
|
FA520A |
Hyperbranched Polyester Compounds |
Efficiently Improve |
PA6,PA66,High-Temperature Nylon Long Chain Nylon |
|
F1530A |
Organosilicone Oxide Polymer |
Efficient Demoulding Performance |
PA,PBT,PET,PC+Fiber,ABS+Fiber |
|
FE550A |
Ethylene Acrylic Acid Copolymer |
Improve Luster,Increase |
PA,PBT,PET,PC+Fiber,ABS+Fiber |
|
GF |
FE 550A |
|
Tensile Strength in yield(MPa) |
Tensile Strain (%) |
Flexual modulus (MPa) |
Flexural strength (MPa) |
Notched Izod (J/m) |
HDT(C) |
| Montan- Wax | ||||||||
|
40 |
- |
- |
180.2 |
2.46 |
10944.07 |
264.24 |
113.239 |
210.4 |
|
40 |
0.8 |
- |
179.04 |
2.4 |
11189.17 |
253.91 |
113.634 |
211.8 |
|
40 |
- |
0.8 |
182.43 |
2.13 |
11575.62 |
245.24 |
109.099 |
211.9 |
FE550A Used inPET+glass fiber
|
GF |
FE550A |
|
Tensile Strength in yield(MPa) |
Tensile Strain (%) |
Flexual modulus (MPa) |
Flexural strength (MPa) |
Notched Izod (J/m) |
HDT(℃) |
| Montan- Wax | ||||||||
|
40 |
- | - |
143.98 |
2.41 |
11960.63 |
213.04 |
76.873 |
77.5 |
|
40 |
0.8 |
- |
139.2 |
3.06 |
11611.57 |
216.74 |
98.266 |
77.2 |
|
40 |
- |
0.8 |
139.71 |
1.98 |
12529.85 |
222.41 |
76.341 |
77.3 |
Its working principle is shown in the figure
This product is mainly suitable for polyamide series (PA6, PA66, PA6T, PA9T, PA10T and other high-temperature nylon, long chain nylon).
▶▶ FA520A Features
Molecular structure: Hyperbranched structure; General formula of main molecule: Cn1Hn2On3; Molecular weight: 250-600; Mesh number: 40-200 mesh; Branching degree 0.61-0.72; Decomposition temperature: 386.4 ℃; Density: 1.3000g/cm.